PolySmooth™
Last updated
Was this helpful?
Last updated
Was this helpful?
PolySmooth™ is a unique, easy-to-print filament designed for hands-free post processing. The surface can be smoothed with alcohol to achieve layer free models using the Polysher™.
PHYSICAL PROPERTIES
Density
ISO1183, GB/T1033
1.10 g/cm3 at 23°C
Melt index
210°C, 2.16kg
6.7 g/10min
Light transmission
N/A
N/A
Flame retardancy
N/A
N/A
CHEMICAL RESISTANCE DATA
Effect of weak acids
Not Available
Effect of strong acids
Not Available
Effect of weak alkalis
Not Available
Effect of strong alkalis
Not Available
Effect of oils and grease
Not Available
Note:
Good: Material may get minor attack after long periods of storage with chemical at ambient temperature
Fair: Material can be used for short time contact with chemical at ambient temperature
Poor: Material becomes unstable on contact with chemical at ambient temperature
MOISTURE ABSORPTION CURVE
THERMAL PROPERTIES
Glass transition temperature
DSC,10°C/min
70℃
Melting temperature
DSC,10°℃/min
N/A
Crystallizatio temperature
DSC,10℃/min
N/A
Decomposition temperature
TGA,20°℃/min
260℃
Vicat softening temperature
ISO 306,GB/T 1633
70℃
Heat deflection temperature
ISO 75 1.8MPa
66℃
Heat deflection temperature
ISO 75 0.45MPa
68℃
PolySmooth™
MECHANICAL PROPERTIES
Young’s modulus (X-Y)
ISO 527, GB/T 1040
2199 ± 43 MPa
Young’s modulus (Z)
ISO 527, GB/T 1040
2010 ± 69 MPa
Tensile strength (X-Y)
ISO 527, GB/T 1040
51.8 ± 0.7 MPa
Tensile strength (Z)
ISO 527, GB/T 1040
38.9 ± 0.8 MPa
Elongation at break (X-Y)
ISO 527, GB/T 1040
14.5 ± 2.9 %
Elongation at break (Z)
ISO 527, GB/T 1040
2.8 ± 0.3 %
Bending modulus (X-Y)
ISO 178, GB/T 9341
2198 ± 57 MPa
Bending modulus (Z)
ISO 178, GB/T 9341
N/A
Bending strength (X-Y)
ISO 178, GB/T 9341
75.9 ± 0.8 MPa
Bending strength (Z)
ISO 178, GB/T 9341
N/A
Notched Charpy impact strength (X-Y)
ISO 179, GB/T 1043
3.1 ± 0.8 kJ/m2
Notched Charpy impact strength (Z)
ISO 179, GB/T 1043
N/A
RECOMMENDED PRINTING CONDITIONS
Nozzle temperature
190 – 220 (℃)
Build surface treatment
PC and Texture PEI (Glue when needed)
Build plate temperature
25 - 70 (˚C)
Cooling fan
ON
Printing speed
50 - 200 (mm/s)
Retraction distance
1 - 3 (mm)
Retraction speed
20 - 40 (mm/s)
Closure Chamber
No Needed
Recommended support material
PolyDissolve™ S1
Drying setting
50˚C for 12h
Annealing setting
-
* Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters
* Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters
Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters
It is highly recommended to use the PolyBox™ when printing with PolySmooth™ and to store it in the resealable bag.
ISO 527, GB/T 1040
HOW TO MAKE SPECIMENS
Bed temperature
60 °C
Shell
2
Top & bottom layer
3
Infill
100 %
Environmental temperature
Ambient temperature
Cooling fan
ON
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End- use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/ recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage, injury or loss induced from the use of Polymaker materials in any application.