Polylite™ PLA Pro is a first of its kind combining high toughness and high rigidity, this professional PLA offers engineering properties with the ease of print of regular PLA.

PHYSICAL PROPERTIES

Property
Testing Method
Typical Value

Density

ISO1183,GB/T1033

1.22 g/cm3 at 21.5℃

Melt index

210℃,2.16kg

6g/10min

Light transmission

N/A

N/A

Flame retardancy

N/A

N/A

CHEMICAL RESISTANCE DATA

Property
Testing Method

Effect of weak acids

Not resistant

Effect of strong acids

Not resistant

Effect of weak alkalis

Not resistant

Effect of strong alkalis

Not resistant

Effect of organic solvent

No data available

Effect of oils and grease

No data available

MOISTURE ABSORPTION CURVE

Property
Testing Method
Typical Value

Glass transition temperature

DSC, 10°C/min

62 °C

Melting temperature

DSC, 10°C/min

150 °C

Crystallization temperature

DSC, 10°C/min

N/A

Decomposition temperature

TGA, 20°C/min

N/A

Vicat softening temperature

ISO 306, GB/T 1633

62.7 °C

Heat deflection temperature

ISO 75 1.8MPa

57.6 °C

Heat deflection temperature

ISO 75 0.45MPa

59.3 °C

Thermal conductivity

N/A

N/A

Heat shrinkage rate

N/A

N/A

Property
Testing Method
Typical Value

Young’s modulus (X-Y)

ISO 527, GB/T 1040

2932.2 ± 55.3 MPa

Young’s modulus (Z)

ISO 527, GB/T 1040

2633.0 ± 117.4 MPa

Tensile strength (X-Y)

ISO 527, GB/T 1040

49.8 ± 0.4 MPa

Tensile strength (Z)

ISO 527, GB/T 1040

36.5 ±0.6 MPa

Elongation at break (X-Y)

ISO 527, GB/T 1040

6.3 ± 0.9 %

Elongation at break (Z)

ISO 527, GB/T 1040

2.4 ± 0.3 %

Bending modulus (X-Y)

ISO 178, GB/T 9341

2933.8 ± 78.3 MPa

Bending modulus (Z)

ISO 178, GB/T 9341

N/A

Bending strength (X-Y)

ISO 178, GB/T 9341

77.9 ± 0.4 MPa

Bending strength (Z)

ISO 178, GB/T 9341

N/A

Charpy impact strength (X-Y)

ISO 179, GB/T 1043

17.1 ±1.2 kJ/m2

Charpy impact strength (Z)

ISO 179, GB/T 1043

N/A

  • Based on 0.4 mm nozzle and Simplify 3D v.4.0. Printing conditions may vary with different nozzle diameters

Parameter

Nozzle temperature

190 – 220 (℃)

Build surface material

BuildTak®, Glass, Blue Tape

Build surface treatment

Glue or Magigoo

Build plate temperature

30 - 60 (˚C)

Cooling fan

ON

Printing speed

30-70 (mm/s)

Raft separation distance

0.2 (mm)

Retraction distance

1 - 3 (mm)

Retraction speed

30 - 60 (mm/s)

Environmental temperature

0 - 40 (˚C)

Threshold overhang angle

60 (˚)

Recommended support material

PolySupport™ and PolyDissolve™ S1

TENSILE TESTING SPECIMEN

ISO 527, GB/T 1040

FLEXURAL TESTING SPECIMEN

ISO 178,GB/T 9341

IMPACT TESTING SPECIMEN

ISO 179,GB/T 1043

*All specimens were conditioned at room temperature for 24h prior to testing

Printing temperature
210 °C

Bed temperature

25 °C

Shell

2

Top & bottom layer

4

Infill

100 %

Environmental temperature

25 ˚C

Cooling fan

ON

DISCLAIMER:

The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End- use performance of printed parts depends not only on materials, but also on part design,environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.

Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/ recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage,injury or loss induced from the use of Polymaker materials in any application.

Last updated

Was this helpful?